Value Units Test Method / Conditions Melt Flow Rate (190°C / 2.16 kg) 0.7 g/10 ASTM D 1238 Melt Flow Rate (190°C/21.6 kg) 50 g/10 min ASTM D 1238 Density 0.962 g/cm³ ASTM D 792 - Typical Properties - Plaque Properties
Value Units Test Method / Conditions Tensile Strength at Yield ᵃ 32 MPa ASTM D 638 Tensile Strength at Break ᵃ 22 MPa ASTM D 638 Flexural Modulus (1% secant) ᵇ 1600 MPa ASTM D 2240 Hardness ᶜ 64 - ASTM D 1693 Izod Impact Strength ᵇ 89 J/m ASTM D 256 Environmental Stress Cracking Resistance (notch 0.3 mm, at 50°C, 10% Igepal CO630) ᵃ 19 h/F50 ASTM D 1693 Environmental Stress Cracking Resistance (notch 0.3 mm, at 50°C, 100% Igepal CO630) ᵃ 24 h/F50 ASTM D 1693 Deflection Temperature (under load, at 0.455 MPa) ᵇ 79 °C ASTM D 648 Vicat Softening Temperature (at 10 N)ᵇ 128 °C ASTM D 1525 - Note
- Test specimens from compression molded plaque according to ASTM D4703.
- Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break.